Endomimetics (United States)

Introduction: Intracranial aneurysms are associated with local degradation of the vessel wall resulting in the formation of a blood-filled sac. Approximately 6 million people are estimated to have intercranial saccular aneurysms in the US alone. Most aneurysms remain undetected until rupture, resulting in hemorrhage which carries a high mortality rate (>50%). Flow diverters are placed across the aneurysm neck to divert blood flow away from the sac, preventing rupture once occluded. However, flow diverters carry significant risk for thromboembolism, which is a major cause of morbidity. The elevated risk of thromboembolism is likely due to endothelial injury of the parent artery at the neck of the aneurysm. We hypothesize that the bionanomatrix can promote faster endothelialization and aneurysm occlusion thereby reducing the risk of thromboembolism after flow diverter treatment. Methods: The bionanomatrix is composed of peptide amphiphiles containing endothelial cell adhesive ligand (YIGSR) and a nitric oxide (NO) donor (KKKKK), both components critical for recruiting and retaining endothelial cells on the device. The NO releasing bionanomatrix was coated onto the flow diverters using ultrasonic spray coating, and the NO effects on endothelial cell (EC) and smooth muscle cell (SMC) proliferation on the coated devices was assessed, in vitro, using calcien-AM staining. For the in vivo study, an elastase-induced rabbit aneurysm model was created. The bionanomatrix coated and uncoated flow diverters were implanted into the rabbit aneurysm model for 4 weeks. The coated and uncoated flow diverters were then analyzed for endothelialization, smooth muscle cell proliferation, and aneurysm occlusion by angiography, gross image, and immunohistochemistry analyses. Results: In vitro, the bionanomatrix coated flow diverters significantly enhanced endothelial cell proliferation as well as reduced smooth muscle cell proliferation on the flow diverters compared to the uncoated device. In vivo, after 4 weeks, the bionanomatrix coated flow diverters demonstrated enhanced neck coverage, more complete endothelialization, and reduced smooth muscle thickness on the coated flow diverters compared to the uncoated devices as seen by gross image analysis and histology. Conclusions: The bionanomatrix coated flow diverters can successfully promote faster endothelialization and brain aneurysm occlusion which is critical for reducing the risk of thromboembolism after neurointervention.

Hemorrhagic blood loss from traumatic injury is the leading cause of death in severe accidents and combat injuries. Treating and stopping blood loss in a timely and effective manner is essential for the survival of the patient. Currently, QuikClot and dry fibrin sealant dressing are well-known approaches for hemostatic treatment. However, these dressings have limitations in slowing blood loss such as being brittle, low blood absorption, and a poor sealant of the injury site. Temperature-sensitive gels may have potential as a platform for delivery of coagulation factors to improve hemostasis and wound sealing in the treatment of traumatic injuries. Here, we developed a temperature-sensitive triblock copolymer (poly ethylene oxide (PEO)-poly propylene oxide (PPO)-poly ethylene oxide (PEO)) containing fibrinogen to promote blood coagulation through gel formation at body temperature. This temperature sensitive solution-to-gel (sol-gel) transition does not require cross-linking agents or UV photoinitiation. We determined that 22 wt % (weight percent) copolymers with and without fibrinogen was the maximum concentration for sol-gel transition at body temperature. Rheology results further confirmed this sol-gel transition of 22 wt % copolymers at body temperature. We showed that fibrinogen itself promoted blood coagulation. Additionally, 22 wt % copolymer with fibrinogen successfully demonstrated stable blood coagulation within the gel compared to 22 wt % copolymer without fibrinogen. Twenty-two weight percent copolymers with and without fibrinogen also exhibited excellent biocompatibility based on cell viability, proliferation, and morphology analysis. In addition, treatment of 22 wt % copolymers did not stimulate pro-inflammatory TNF-α production from differentiated human monocytes. Our results suggest that 22 wt % of a temperature-sensitive copolymer gel containing fibrinogen has great potential as a hemostatic agent stimulating coagulation and providing immediate wound coverage for protection through a sol-gel transition at body temperature.

We report a novel and facile organosilane plasma polymerization method designed to improve the surface characteristics of poly(tetrafluoroethylene) (PTFE). We hypothesized that the polymerized silane coating would provide an adhesive surface for endothelial cell proliferation due to a large number of surface hydroxyl groups, while the large polymer networks on the surface of PTFE would hinder platelet attachment. The plasma polymerized PTFE surfaces were then systematically characterized via different analytical techniques such as FTIR, XPS, XRD, Contact angle, and SEM. The key finding of the characterization is the time-dependent deposition of an organosilane layer on the surface of PTFE. This layer was found to provide favorable surface properties to PTFE such as a very high surface oxygen content, high hydrophilicity and improved surface mechanics. Additionally, in vitro cellular studies were conducted to determine the bio-interface properties of the plasma-treated and untreated PTFE. The important results of these experiments were rapid endothelial cell growth and decreased platelet attachment on the plasma-treated PTFE compared to untreated PTFE. Thus, this new surface modification technique could potentially address the current challenges associated with PTFE for blood contact applications, specifically poor endothelial cell growth and risk of thrombosis.