This work presents a detailed description of a bonding zone of explosively welded Ti/steel clads subjected to stress relief annealing, applied in order to improve the plasticity of the final product. The typical joint formed by the welding process possesses a characteristic wavy interface with melted regions observed mainly at the crest regions of waves. The interface of Ti/steel clads before and after annealing was previously investigated mostly in respect to the melted regions. Here, a sharp interface between the waves was analyzed in detail. The obtained results indicate that the microstructure of a transition zone of that area is different along the width. After the heat treatment at 600 °C for 1.5 hours, titanium carbide (TiC) together with α-Fe phase forms at the interface in local areas of relatively wide interlayer (~ 1 µm), while for most of the sharp interface, a much thinner zone up to about 400 nm, formed by four sublayers containing intermetallic phase and carbides, is present. This confirms that carbon diffusion induced by applied heat treatment significantly influences the final microstructure of the Ti/steel interface zone. Side bending tests confirmed high plasticity of welds after applied heat treatment; however, the microhardness measurements indicated that the strengthening of the steel in the vicinity of the interface had not been removed completely.

Abstract This paper assesses the effect of various values of detonation velocity on the quality of the bond zone, and thus the properties of bimetal zirconium (Zr 700) - steel (P355NL). The research was carried out for as-bonded welds, i.e. immediately following explosion welding. The results of shearing, peeling and tensile tests as well as macro-scale structural analyses were presented. In order to determine the changes in the value of strain hardening, the microhardness measurements across the interface were carried out. Based on the performed analyses it can be claimed that, depending on the applied technological settings of welding, most cases displayed wavy bond with highly diversified parameters of the wave. The changes observed with the detonation velocity are non-monotonic. High detonation velocities favored the formation of waves with large height and length and strongly affect the increase of the volume of brittle melted zones. Increased volume of the melted regions results in strong decrease of strength properties of the clad. The analysis of strength test results allows claiming that a small volume of melted regions in the bond considerably improves the strength of the bond.As a result of explosion welding, strain hardening of the joined materials occurs near the interface. In the case of clad fabricated using high technological parameters the increase of strengthening and the depth of its influence in the interface area is observed.

The problem of a small current-carrying loop situated over a thin plane sheet of conducting material is solved. The cases are considered where the loop axis is oriented both perpendicular and parallel to the plane of the sheet.