The phase transformation behavior from austenite upon cooling in a 1.5Mn-1.5Si-0.2C steel was in situ monitored using dilatometry, X-ray and neutron diffractions. The starting temperature of ferrite transformation was in good agreement between dilatometry and neutron diffraction, whereas much higher in X-ray diffraction. Such a discrepancy in transformation temperature is attributed to the change in chemical composition near the surface of a specimen heated to elevated temperatures in a helium gas atmosphere for X-ray diffraction. In situ neutron diffraction enables us to investigate the changes in lattice constants of ferrite and austenite, which are affected by not only thermal contraction but also transformation strains, thermal misfit strains and carbon enrichment in austenite. Pearlite transformation started after carbon enrichment in austenite reached approximately 0.7 mass% and contributed to diffraction line broadening.

ABSTRACT Applications of neutron diffraction to microstructure evaluation of steel investigated by a project commissioned by the Innovative Structural Materials Association are summarized. The volume fraction of austenite (γ) for a 1.5Mn-1.5Si-0.2C steel was measured by various techniques including backscatter electron diffraction (EBSD) and X-ray diffraction. It is recommended to measure volume fraction and texture simultaneously using neutron diffraction. The γ reverse transformation was in situ monitored using dilatometry, EBSD, X-ray diffraction and neutron diffraction. The γ reversion kinetics showed excellent agreements between dilatometry and neutron diffraction, whereas the γ formation started at higher temperatures in EBSD and X-ray diffraction measurements. Such discrepancy is attributed to the change in chemical compositions at the specimen surface by heating; Mn and C concentrations were decreased with heating. Phase transformations from γ upon cooling were monitored, which enabled us to elucidate the changes in lattice parameters of ferrite (α) and γ affected by not only thermal contraction but also transformation strains, thermal misfit strains and carbon enrichment in γ in the above hypoeutectoid steel. Pearlitic transformation started after the carbon enrichment reached approximately 0.76 mass% and contributed to diffraction line broadening. Martensitic transformation with or without ausforming at 700°C was monitored for a medium carbon low alloyed steel. Dislocation density after ausforming was determined using the convolutional multiple whole profile fitting method for 10 s time-sliced data. The changes in γ and martensite lattice parameters upon quenching were tracked and new insights on internal stresses and the axial ratio of martensite were obtained.