Nanova Biomaterials (United States)

The objective of this study is to evaluate the plasma treatment effects on oral fungal biofilms. Candida albicans biofilms were developed on the 48-well plate to serve as a model of oral fungal biofilm. The treatment of 0.2% chlorhexidine digluconate (CHX) was used as a positive control compared with plasma treatments. The efficacy of treatments was determined by 3-(4,5-dimethylazol-2-yl)-2,5-diphenyl-2H-tetrazolium bromide (MTT) assay and confocal laser scanning microscope (CLSM). The survival percentage of Candida albicans decreased from 52% to 27% as the plasma power increased from 6mA to 8mA and plasma exposure time extended from 2 min to 10 min. Moreover, it was found that there is a synergistic effect of the combination of plasma and CHX treatments. Scanning electron microscopy (SEM) examination indicated severe cell damages resulting from plasma treatment. In conclusion, the low-temperature plasma treatment is effective in deactivating Candida albicans biofilms and thus provides a promising alternative to disinfect oral fungal biofilms.

The ideal scaffold for bone repair should have a hierarchical pore structure and gradient degradation performance to satisfy the uniform adhesion and proliferation of cells in the scaffold at the early stage of implantation, as well as providing space for the subsequent regeneration of bone tissue. To this end, we developed a hierarchical polylactic acid glycolic acid copolymer (PLGA)/nano-hydroxyapatite (n-HA)/gelatin (Gel) (PHG) scaffold with a printed PLGA/n-HA (PH) framework and a Gel network filler for bone regeneration by the combination of 3D printing and freeze-drying technologies. The fabricated PHG scaffold features large front hole size (>1100 μm × 1100 μm) and side hole size (>500 μm) to provide sufficient open space and reliable integrated support for cell and tissue ingrowth. The gelatin network filled in the PH framework played the role of a cell holder just like an extracellular matrix (ECM) in the early stage. In vitro degradation experiments revealed that the gelatin network completely degraded within 5 weeks while the structural integrity of the framework still remained at the 32nd week. The results of cell culture confirmed that the PHG scaffold was more conducive to cell attachment. In vivo assessments in a rat femoral defect model showed that PHG scaffolds were more favored for new bone formation and achieving a tighter bond between the scaffold and the original tissues. The hierarchical PHG scaffold has great application potential in bone tissue engineering and will provide a reference for the model design of bone scaffolds.

To solve the high instances of failure caused by endodontic reinfection, herein, an improved root filling material was produced to meet the multi-functional demand of sealers for root canal therapy. In this study, polyurethane (PU)-based nanocomposites were prepared by loading bismuth oxide, hydroxyapatite and antibacterial agents, namely Ag3PO4 and ZnO nanoparticles, which were named CP-Ag and CP-Zn sealers, respectively. A parallel biological evaluation at bacterial and cellular levels was performed to determine the fate of the different components of the PU-based sealers. Furthermore, the composition of sealers was quantified by screening their antibacterial activity and apoptotic factors, considering the potential toxicity of the nanoparticles and high dosage of metals. The in vitro optimization investigation was conducted systematically against Streptococcus mutans and Staphylococcus aureus, including bacteriostatic and dynamic tests, and the expression of the B-cell lymphoma-2 gene family and caspase proteases in the mitochondria-mediated apoptotic pathway was evaluated using the commercial AH Plus® and Apexit® Plus sealers for comparison. Additionally, the physical properties and sealing ability of sealers were assessed. The results showed that all PU-based sealers could meet the requirements of ISO 6876:2012 for root canal sealing materials. Based on the evaluation system, CP-Zn sealers expressed longer lasting antibacterial activity and lower toxic effect on cells compared to CP-Ag sealers. Especially, the CP-Zn5 sealer exhibited selective antimicrobial efficacy and hypo-toxicity, which were better than that of the two commercial sealers. According to the two-dimensional and three-dimensional methods, the good sealing ability of the CP-Zn5 sealer is the same as the excellent filling characters of AH Plus, which adapts to irregular root canals.

ABSTRACTManagement of dental plaque/biofilms is critical to maintain oral health. The objective of this study is to investigate the treatment effects of non-thermal atmospheric gas plasmas on oral biofilm formation and recovery under in vitro and in vivo conditions. Streptococcus mutans biofilms, a significant contributor to tooth decay, were cultured and treated by plasma. It was found that plasma treatment not only significantly reduced the in vitro biofilms, but also increased the metabolic activity of the bacteria in the biofilms. As compared with untreated control group, the cell metabolic activity, as measured by MTT assay, increased by 273%, and the aconitase activity increased by 446% for the plasma-treated group. The increased metabolic activity of the plasma-treated biofilm bacteria enhanced their susceptibility to antibiotic and host defense. An in vivo animal model using a total of 60 female rats (19 days old) were used to evaluate the anti-caries effects on the molars by 2 min of plasma treatment. It was found that, 6 months after the plasma treatment, the decayed surfaces were reduced by 62.5% on the upper molars and by 31.6% on the lower molars as compared with the untreated upper and lower molars, respectively. These in vitro and in vivo data demonstrate that the physiological state change of the biofilm due to plasma treatment provided benefit to caries control and prevention.