Shofu (Japan)

This study evaluated the efficacy of S-PRG vanishes on preventing enamel demineralization. Bovine enamel specimens were obtained, polished and the baseline Knoop microhardness was evaluated. Specimens were stratified into six groups (n = 15), according to the varnish applied: S10—experimental varnish containing 10% of S-PRG fillers, S20—20% of S-PRG fillers, S30—30% of S-PRG fillers; S40—40% of S-PRG fillers; PC (positive control)—5% of NaF; NC (negative control)—no treatment was performed. Half of enamel surfaces were protected to work as a control and varnishes were applied over the unprotected area. A demineralizing pH-cycling was performed, and surface and cross-sectional microhardness were measured. The percentage of microhardness of the treated area was calculated comparing with the untreated area. Statistical analysis was performed by one-way ANOVA and Tukey’s test (p = 5%). All experimental S-PRG varnishes protected against demineralization in relation to no treatment, but S40 was the most effective on the surface. For all depths, S30 and S40 were superior in enamel demineralization prevention than other S-PRG filler concentrations and 5% NaF. It was concluded that S-RPG filler containing varnishes were effective to prevent enamel demineralization. The higher concentrated products were more effective than 5% sodium fluoride on surface demineralization prevention.

Aim: To examine the relation wear resistance and microhardness of composite block, hybrid block, resin composite to provide convenient argument to clinical usage of materials. Methods: Conventional resin composite (IPS Empress direct, Ivoclar Vivadent), hybrid ceramic block (Enamic, Vita) and composite blocks (Lava Ultimate, 3M), (Hc block, Shofu), (BrilliantCrios, Coltene), (Cerasmart, GC) were investigated. Specimens (n=12 for each group) (n=12 for each group) were loaded in a chewing simulator together a thermal cycling (49 N force, 240.000 cycles, 1.5 mm lateral movement, 1.7 Hz frequency). Specimens were scanned with a Las-20 (Laserscanner, SD Mechatronic) and Vickers microhardness (VHN) was determined (200 grf, 10 s). Statistical analysis was performed with using spearman correlation coefficient. Results: A negative correlation determined for all groups (r=- 0.83). Correlation was observed only composite block group between microhardness and wear resistance and no correlation was found hybrid block and resin composite. Conclusion: Correlation has found between surface microhardness and abrasive wear resistance of the IPS Empress direct,Enamic, Brilliant Crios, Hc block, Cerasmart, Lava Ultimate materials.

著者らは揮発性の酢酸イソアミルが抗菌活性を示すことを見出した。酢酸イソアミルはよく知られた清酒の吟醸香の主成分であり，清酒醸造において非常に興味深い発見である。揮発性酢酸イソアミルの各種食品汚染微生物に対する生育阻害活性とそのメカニズムに関する一連の研究について解説していただいた。

Calprotectin, an inflammation-related protein, is present in gingival crevicular fluid (GCF), and the determination of calprotectin is useful for diagnosing periodontal diseases. The authors have recently developed a novel immunochromatographic (IC) chip system to determine calprotectin levels in GCF. In the present study, the usefulness of this diagnostic system is investigated in patients with periodontal diseases. Thirty-six patients with periodontal diseases participated in this clinical test at multiple centers. Periodontitis sites (n=118) and non-periodontitis (healthy) sites (n=120) were selected after periodontal examination. GCF collection and periodontal examination were performed at baseline, after supragingival and subgingival scaling and root planing. Calprotectin levels in GCF were determined using a novel IC chip system and evaluated as a visual score and an IC reader value. Correlations between GCF calprotectin levels, clinical indicators, and changes in calprotectin levels by periodontal treatments were investigated. Receiver operating characteristic (ROC) analysis of IC reader value for GCF calprotectin was performed to predict periodontal diseases. The visual score of GCF calprotectin was highly correlated with the IC reader value. IC reader values of GCF calprotectin in the periodontitis group were higher than those of the healthy group at three dental examination stages, and they significantly decreased with periodontal treatments. Visual scores and IC reader values of GCF calprotectin were correlated to levels of clinical indicators. ROC analysis for GCF calprotectin showed an optimal cutoff value to predict periodontal diseases. Determination of GCF calprotectin using a novel IC chip system is useful for diagnosis of periodontal diseases.

In dentistry, a wide range of materials is available for restorative treatment; a typical product of such restorative materials mainly consists of radically polymerizable monomer(s) and inorganic filler(s) (for added physical strength), as well as a surface modifier (e.g. silane coupling agent) for improved affinity between monomer and filler. It is favorable to use an optimal surface modifier depending on the respective restorative materials. However, commercially available surface modifiers, which are synthesized by the ton, are not always suited for what is required for properties of the many different dental restorative materials. As a potential solution to such a problem, we focused on the latest technology, “micro flow reactors” that enabled an on-demand low-volume synthesis of many types of surface modifiers. Using micro reaction fields of such flow reactors, we synthesized a novel long-chain silane coupling agent. Compared to the control system synthesized using a conventional reaction flask, the novel system enabled significant reduction in reaction time without inducing any major side reactions. A dental composite resin that was treated with the novel coupling agent exhibited higher toughness, suggesting that such a silane coupling agent was an effective surface modifier.

The behavior of water-soluble photoinitiators with crown ethers in dental adhesives is unknown. This study investigated the effect of sodium acylphosphine oxide (APO-Na) with crown ether in a hydrophobic adhesive on adhesion to teeth. Sodium 2,4,6-trimethylbenzoyl-phenylphosphine oxide (TMPO-Na = APO-Na) was synthesized in 67.1% yield and identified by 1H NMR. APO-Na was dissolved in hydrophobic resins in the presence of a crown ether (ionophore effect). Thirty kinds of experimental single-step adhesives comprising APO-Na, CE, Bis-GMA, 6-methacryloyloxyhexyl phosphonoacetate (6-MHPA), and 4-methacryloyloxyethyl trimellitic acid (4-MET) were thereby prepared. Shear bond strength to unetched ground teeth was measured at a crosshead speed of 1.0 mm/min, and the data were analyzed by ANOVA. The shear bond strength results of bonding resins containing APO-Na with 18-crown-6-ether (CE-6) were significantly higher than that without CE-6 (control) (p<0.05). Higher bond strength values [for enamel: BR24 at 19.3 (3.2) MPa; for dentin: BR29 at 20.2 (4.7) MPa] were achieved with the adhesives containing APO-Na, CE-6, 6-MHPA, and 4-MET. Therefore, it was found that APO-Na with CE-6 contributed to the efficient bonding performance of single-step adhesive to teeth. However, in view of the biosafety hazard posed by crown ethers, the search is still on for reagents that are biologically safer than crown ethers--but with ionophor effects--to be used in dental adhesives.

A novel ethyl methacrylate (EMA) resin was developed to overcome the tissue, organ and systemic damage associated with the residual monomer of conventional methyl methacrylate (MMA) resin bone cement. EMA resin is a chemical/ photopolymerizable material and is easy to handle during clinical procedures. The biocompatibility of EMA was evaluated in accordance with ISO10993-6. No inflammatory response was observed 1 and 9 weeks after implantation in the dorsal subcutaneous tissue of ddY mice. EMA resin also demonstrated better biocompatibility when compared with conventional bone cements. Poly-L-lactic acid (PLLA) was used as a carrier for bone morphogenetic protein (BMP) and added to the EMA slurry. The EMA-PLLA composite membrane was sticky and BMP readily adhered to its surface. The EMA-PLLA-BMP composite membrane induced new bone formation, the new bone growing in the shape of the EMA in the thigh muscle pouch of ddY mice. This novel EMA resin has many potential clinical applications.