Capturing Age-Dependent Properties of Human Skin Using Magnetorheological Elastomers

Modified silane-coated carbonyl iron/natural rubber composite elastomer and its magnetorheological performance

Influence of composition of carbonyl iron particles on dynamic mechanical properties of magnetorheological elastomers

Effects of iron particles’ volume fraction on compression mode properties of magnetorheological elastomers

The effect of a uniform magnetic field on the permittivity of magnetorheological elastomers (MREs) is studied. MREs were synthesized on the basis of silicone rubber and magnetic fillers of various chemical nature (Fe, NdFeB and Fe3O4) and particle sizes. The value of permittivity was obtained from the measurements of the capacity of a plane capacitor with MRE samples. A strong increase of the permittivity (magnetodielectric effect) was observed when the applied field was perpendicular to the capacitor plates. The value of the magnetodielectric effect was found to be strongly dependent on the type of magnetic filler as well as on the size and concentration of magnetic particles within MRE composites. The highest magnetic response reaching 150% was observed for the MRE based on a magnetically hard NdFeB filler. A simple model explaining physical reasons for the magnetodielectric effect in a MRE is proposed. The developed MRE with a strong magnetodielectric effect is very promising for a wide range of applications, in particular, as magnetic field sensors and actuators.

This study presents the dynamic numerical model of magneto-rheological elastomers (MREs) along with the dynamic testing of the material under various loading conditions. Primarily the loading in shear mode is considered in this study because many civil engineering structures are subjected to shear loading. Experimental tests were carried out in order to characterize the dynamic behavior of MREs. A test setup was designed and fabricated to load the MRE samples in shear mode with varying magnetic fields. A series of shear tests of MRE samples were performed under various magnetic field values, amplitudes and frequencies of loading. The test results show that the material stiffness is increased with increasing magnetic field and loading frequency within the ranges of the magnetic field and exciting frequency considered in this work. Based on the experimental results, a dynamic model was developed to capture the dynamic behavior of the MRE.

Magnetorheological elastomers (MREs) are a type of smart material that can change their mechanical properties in response to external magnetic fields. These unique properties make them ideal for various applications, including vibration control, noise reduction, and shock absorption. This paper presents an approach for modeling the impact behavior of MREs. The proposed model uses a combination of exponential functions arranged in a multi-layer Preisach model to capture the nonlinear behavior of MREs under impact loads. The model is trained using particle swarm optimization (PSO) and validated using experimental data from drop impact tests conducted on MRE samples under various magnetic field strengths. The results demonstrate that the proposed model can accurately predict the impact behavior of MREs, making it a useful tool for designing MRE-based devices that require precise control of their impact response. The model's response closely matches the experimental data with a maximum prediction error of 10% or less. Furthermore, the interpolated model's response is in agreement with the experimental data with a maximum percentage error of less than 8.5%.

This article focuses on evaluating the influence that the addition of carbonyl iron micro-particles (CIPs) and its alignment have on the mechanical and rheological properties for magnetorheological elastomers (MREs) fabricated using polydimethylsiloxane (PDMS) elastomer, and 24 wt % of silicone oil (SO). A solenoid device was designed and built to fabricate the corresponding composite magnetorheological material and to perform uniaxial cyclic tests under uniform magnetic flux density. Furthermore, a constitutive material model that considers both elastic and magnetic effects was introduced to predict stress-softening and permanent set effects experienced by the MRE samples during cyclic loading tests. Moreover, experimental characterizations via Fourier transform infrared (FTIR), X-ray diffraction (XRD), tensile mechanical testing, and rheological tests were performed on the produced MRE samples in order to assess mechanical and rheological material properties such as mechanical strength, material stiffness, Mullins and permanent set effects, damping ratio, stiffness magnetorheological effect (SMR), and relative magnetorheological storage and loss moduli effects. Experimental results and theoretical predictions confirmed that for a CIPs concentration of 70 wt %, the material samples exhibit the highest shear modulus, stress-softening effects, and engineering stress values when the samples are subject to a maximum stretch value of 1.64 and a uniform magnetic flux density of 52.2 mT.

Magnetorheological elastomer (MRE) is a new kind of smart materials, its dynamic mechanic performances can be controlled by an applied magnetic field. MRE is usually used as a stiffness-changeable spring in the semi-active vibration absorber. In order to get perfect vibration control effect, low dynamic damping of MRE is need. But the dynamic damping of MRE was not studied deeply in the past. The dynamic damping of MRE was studied and analyzed. The influences of different test conditions including test strain amplitude, test frequency and test magnetic field were deeply studied. MRE sample and pure silicone rubber sample were prepared and tested under different conditions. The test results show that the main source of dynamic damping is the friction between iron particles and rubber matrix. And the friction is mainly influenced by the strain amplitude and test magnetic field.

Experimental Investigation of Effect of Ingredient Particle Size on Dynamic Damping of RTV Silicone Base Magnetorheological Elastomers

Collecting human skin samples for medical research, including developing microneedle-based medical devices, is challenging and time-consuming. Researchers rely on human skin substitutes and skin preservation techniques, such as freezing, to overcome the lack of skin availability. Porcine skin is considered the best substitute to human skin, but their mechanical resemblance has not been fully validated. We provide a direct mechanical comparison between human and porcine skin samples using a conventional mechano-analytical technique (microindentation) and a medical application (microneedle insertion), at 35% and 100% relative humidity. Human and porcine skin samples were tested immediately after surgical excision from subjects, and after one freeze-thaw cycle at −80 °C to assess the impact of freezing on their mechanical properties. The mechanical properties of fresh human and porcine skin (especially of the stratum corneum) were found to be different for bulk measurements using microindentation; and both types of skin were mechanically affected by freezing. Localized in-plane mechanical properties of skin during microneedle insertion appeared to be more comparable between human and porcine skin samples than their bulk out-of-plane mechanical properties. The results from this study serve as a reference for future mechanical tests conducted with frozen human skin and/or porcine skin as a human skin substitute.

In this study, magnetorheological elastomers (MREs) were synthesized by incorporating various amounts of sucrose acetate isobutyrate (SAIB) ester plasticizer dopped in the epoxidized natural rubber (ENR-50) matrix with constant carbonyl iron particles (CIPs) of 60 weight percent. The effect of SAIB insertion on curing characteristics has been observed using a moving die rheometer. The microstructures appearance of the samples were observed using a field emission scanning electron microscope (FESEM). Finally, the magneto-induced storage modulus was measured by using a rheometer 302. The experimental results have demonstrated that the addition of SAIB ester decreased the cure rate index (CRI) by 63% and increased the MR effect by 37%. Observation of microstructure shows that the CIPs embedded well in the matrix and produced the isotropic structure of the MREs. Meanwhile, the fabricated MREs samples were frequencies dependent, where all MREs samples exhibit the incremental trend when increasing the frequencies. The introduction of SAIB has proven to influence the properties of the MREs.

In this study, 3D printed magnetorheological (MR) elastomer has been characterized through a force vibration testing. The 3D printed MR elastomer is a composite consisting three different materials, magnetic particles and two different elastomers. The MR elastomers were printed layer-by-layer by encapsulating MR fluid within the polymeric elastomer and then allowed to cure at room temperature. The 3D printing allowed to print various patterns of magnetic particles within the elastomeric matrix. In the presence of an external magnetic field, both elastic and damping properties of the 3D printed MR elastomers were changed. Natural frequency, stiffness, damping ratio, damping coefficient, and shear modulus were increased with increasing magnetic field. For the single degree-of-freedoms system, shear mode MR elastomers suppressed the transmitted vibration amplitude up to 31.4% when the magnetic field was 550 mT. The results showed that the 3D printed MR elastomer could be used as a tunable spring element for vibration absorption or isolation applications. However, further optimization of the magnetic particles’ configurations should be performed to obtain the higher MR effect.

The rheological properties of magnetorheological elastomers are influenced by magnetically sensitive fillers and the elastomer matrix. The ability to respond to an external magnetic field is imparted by the fillers, while the load-bearing capability is determined by the matrix type. In this paper, the effect of matrix material on the properties of magnetorhological elastomer is explored experimentally. Carbonyl iron particle content is varied by 0%, 15% and 25% by volume to produce magnetorheological elastomer samples using natural rubber, silicone rubber and nitrile butadiene rubber matrices. Forced transmissibility test approach was employed to evaluate the field induced variations in the dynamic stiffness and loss factor of magnetorheological elastomers. The dynamic stiffness of nitrile butadiene rubber is the highest, while that of silicone rubber is the lowest. Addition of carbonyl iron particles significantly improves stiffness, although these gains depend on the properties of unfilled matrix. The addition of 25% by volume of carbonyl iron particle increased the dynamic stiffness of a silicone rubber matrix based magnetorheological elastomer by 67.78%, while the similar change in magnetorheological elastomer with nitrile butadiene rubber matrix was 38.58%. The field dependent response of magnetorheological elastomers is governed by the matrix and ferromagnetic filler concentration. These qualities are higher in magnetorheological elastomer with a low initial dynamic stiffness matrix and lower in magnetorheological elastomers with a stiffer matrix.

Magnetorheological Elastomer (MRE) is a type of smart composite material consisting of a polymer matrix embedded with ferromagnetic particles. In the presence of an external magnetic field, its mechanical properties, such as stiffness, changes make it attractive in vibration isolation applications. Unwanted vibration in machines can cause severe damage and machine breakdown. In Qatar, the extraction of the natural gas from the ground requires sophisticated drilling machines. In this work, a semi-active vibration isolator using MRE is proposed for a potential application in a drilling system to isolate the torsional vibration. MRE was fabricated with a 35% mass fraction (MF) consisting of silicon rubber and iron particles. It was fitted with aluminum couplers and attached to the shaft (drill string) to study its efficiency in vibration isolation under a magnetic field. Two tests were conducted on the drilling prototype setup used in this work; the first test was a hammer impact test. The torsional transfer function TTF analysis showed that the system's natural frequency has shifted from 13.9 Hz to 17.5 Hz by the influence of increasing magnetic field around the MRE. The results showed that the continuous rotational vibration amplitude of the prototype is attenuated by more than 40%.

Magnetorheological elastomer (MRE) is a novel kind of magnetorheological materials and has been successfully used to control the structure vibration due to its property of variable stiffness under different magnetic field. In order to improve the properties of MRE, it urgently needs to investigate the preparation methods of MRE and build a corresponding test system to evaluate the performance of MRE in different operating modes. In this paper, different magnetic devices for preparing MRE were studied and designed, and the material was fabricated by the permanent magnets with additional permeability equipment at last. Then, according to the SDOF principle, a novel test system was built in order to investigate the mechanical properties of MRE, and exact close-form expressions of the stiffness, loss factor and other mechanical parameters of MRE, under different magnetic field, have been calculated to analyze the properties of MRE.