Modeling Asymmetric Flow in the Thin‐Slab Casting Mold Under Electromagnetic Brake

A submerged entry nozzle (SEN) for thin slab casters operating at casting speeds as high as 7.5 m/minute was developed based on fundamental grounds of boundary-layer theory and water modeling experiments. Experimental techniques included tracer injection to observe overall fluid flow patterns, high speed video camera and image analysis to follow dynamic changes of meniscus levels and particle image velocimetry to measure water speeds in the mold. This design was compared with two other SEN designs of nozzles under current commercial use at various thin slab casters. Direct comparisons of mathematical simulations and experimental results among the three SEN's evidenced that this new SEN yields very stable flows which are independent from casting speed and nozzle immersion depth. Fluid flow developed by this SEN consists of a double roll pattern without generation of superficial vortices. The two other SEN's yield instable discharging jets due to and excessive shearing effects with the surrounding fluid inducing severe dissipation of kinetic energy which promotes severe tailing effects inducing strong meniscus oscillations. The proposed design has reported good industrial performances and a longer operating life because the slag protection belt suffers less wear thanks to smaller velocities of the bath in contact with the SEN wall.

In order to solve problems involved with the curved type continuous caster and high speed casting by controlling the steel flow in the mold, the Electromagnetic Mold Brake Ruler (EMBR) using a static magnetic field was installed and tested at No. 2 continuous casting plant at kwangyang Works, POSCO. The meniscus profile and surface velocity were measured to optimize EMBR operation and slab qualities were inspected under various operating conditions of the equipment, especially using two different types of core. The plant trials showed different results for each core type. High position of core which was a simple linear type located near the Submerged Entry Nozzle (SEN) outlets had a detrimental effect on the surface and internal qualities of slab. But low position of core which has a magnetic insulator at the core center and is located below the SEN reduced the sub-surface defects and non-metallic inclusions in the slab, especially at high throughput casting conditions.

The clogging behavior of submerged entry nozzle (SEN) is the main reason restricting the continuous casting of steel, which seriously affects the application and popularization of rare‐earth (RE) steel. Through literature analysis, herein, the main influencing factors and mechanism of RE steel continuous casting immersion outlet clogging, and sorts out the main ideas and practices of relevant Japanese enterprises in solving SEN clogging in recent years, are summarized, mainly including the following: 1) optimizing SEN materials to reduce nozzle clogging reactions; 2) using Ar‐blowing SEN; 3) applying electromagnetic field to eliminate charge and inhibiting clogging reaction; and 4) and regulating the composition of molten steel to reduce the possibility of clogging, etc. The combination of these advantages and measures is a feasible way to solve the nozzle clogging of RE steel continuous casting nozzle.

Effect of interfacial reaction behaviour on the clogging of SEN in the continuous casting of bearing steel containing rare earth elements

In the current study, a three-dimensinal (3D) numerical model is built to investigate the effect of a local-type electromagnetic brake (EMBr) on the fluid flow, heat transfer, and inclusion motion in slab continuous casting strands. The results indicate that the magnetic force affects the jet characteristics, including jet angle, turbulent kinetic energy, and its dissipation rate. To reduce the top surface velocity and stabilize the top surface, the magnetic flux intensity should be larger than a critical value. With a 0.39 T magnetic flux intensity, the top surface velocity and its fluctuation can be well controlled, and less slag is entrained. The motion of argon bubbles is also studied. More bubbles, especially >2.0-mm bubbles, escape from the top surface between the mold submerged entry nozzle (SEN) and \( \frac{1}{4} \) width for the case with a 0.39 T EMBr. This may push the top slag away and create an open “eye” on the top slag. Small bubbles (≤1 mm) tend to escape from one side of wide face no matter with or without EMBr, which is induced by the swirl flow from the SEN outport. EMBr has a little effect on the overall removal fraction of inclusions; however, it affects the local distribution of inclusion in the slab. With EMBr, more inclusions accumulate the region just below the surface, thus a worse subsurface quality, whereas the inner quality of the slab is better than that without EMBr. For heat transfer in the mold, the heat flux on the narrow face and the area of possible break-out zones can be reduced by using EMBr. Prevention of bias flow and/or asymmetrical flow in mold by EMBr is also concluded.

The melt flow, level fluctuation, temperature field, and solidification behavior coupled with electromagnetic stirring (EMS) effects in the continuous casting mold region of U71Mn steel bloom were numerically analyzed by commercial computational fluid dynamics (CFD) software named ANSYS FLUENT. The effects of submerged entry nozzle (SEN) structures and the installation methods for optimized four-port SEN on the flow pattern, level fluctuation, heat transfer and initial solidification behavior in a bloom mold loaded with EMS were investigated. The aim is to propose a better SEN condition for the big bloom casting of high railway steel. The water simulation experiments were conducted to show the flow characteristics under different SEN conditions and verify the numerical model of flow pattern. The experimental and numerical simulation results showed that the optimized four-port SEN with diagonal installation cannot only improve the flow pattern of the molten steel by alleviating the level fluctuation and reducing the impact pressure to the wall. It is also beneficial for temperature variation at both bloom surface and corner, as well as the local solidified shell thinning phenomena due to the elimination of impingement effect.

Full-scale water modelling studies combined with nail-dipping industrial trials at Shougang Jingtang (SGJT) Works were carried out in order to investigate the parameters that influence flow patterns in the continuous slab casting mould. The effects of casting speed/mould width combinations, argon bubbling flow rates, submerged entry nozzle (SEN) immersion depths and SEN geometries (port angle and bottom shape) on the flow patterns were examined. A CMI factor defined as casting speed/mould width ratio index is put forward to describe the combined effect of these parameters on the fluid flow patterns in the mould. The results show that the CMI and argon injection rates are the dominant factors that determine the flow pattern. On the basis of the results from this study, critical argon flow rates for different casting combinations have been evaluated. These findings provide operating guidelines for generating optimal flow patterns based on double roll flow with appropriate surface velocities in continuous slab casting moulds. On the basis of these considerations, slab quality at SGJT Works was substantially improved and the percentage of flow pattern-related sliver defects in cold rolled products was decreased from 4.5 to 2.3%.

Formation mechanism and control of a kind of pit-shaped defect in Cf53 rolled products

Electromagnetic braking (EMBr) technology, as one of the most effective technologies in the continuous casting process, provides an effective tool for improving the internal and external defects of steel products. Specifically, the EMBr technology takes the benefit of the generation of Lorentz force to decrease flow instability, mold powder entrapment, and surface defects, if applied properly. For this purpose, to gain a clear understanding of the effect of EMBr technology on the continuous casting process, a commonly used EMBr technology, namely ruler EMBr technology, is applied in the current work to investigate the dynamic behaviors of molten steel flow and steel–slag interface fluctuation inside a slab mold. Furthermore, to obtain a desirable braking effect of the ruler EMBr technology, operational parameters including the magnetic flux density, submerged entry nozzle (SEN) depth, and magnetic pole location are numerically investigated. The results demonstrate that the braking effect exerted by the ruler EMBr device is favorable for suppressing the impact of upward stream on the steel–slag interface with the magnetic flux density exceeding 0.3 T. For the influence of the SEN depth and magnetic pole location on the effect of ruler EMBr mold, the results show that a steady jet flow pattern can be obtained through the adjustment of a location between the ruler EMBr device and the SEN depth. For instance, when the ruler EMBr device installation position of 225 mm corresponds to the SEN depth of 150 mm, the upward deflection of jet stream is suppressed and a stable interface fluctuation profile is formed. With this adjustment, the possibility of mold flux entrapment is decreased.

For the purpose of increasing the capacity of an Angang Strip Production (ASP) continuous caster and the surface quality of a medium-thin slab with mold sections of 150 × (1020–1540) mm2, the present work investigated the influences of the submerged entry nozzle (SEN) structure and main operating parameters on the flow characteristic and temperature distribution in the mold by physical and numerical simulations. The results showed that the typical “double-roll” flow and a central jet were formed through the three-port SEN. With the original SEN, the mean wave height exceeded the critical value of 5.0 mm after the casting speed was increased due to the strong upper recirculation flow. By the slight increment of the bottom port area and the side port angle of SEN, the mean wave height was obviously decreased below 4.4 mm due to the depressing of the upper recirculation flow after the casting speed increased. Meanwhile, the temperature distribution was slightly changed by using the optimized SEN. The practical application showed that the breakout rate decreased from 0.349% to 0.107% and the surface defect rate decreased from 0.54% to 0.19% by using the optimized SEN, while throughput reached the new level of 3.96 t/min.

Transient flow structures in a continuous casting mold can strongly influence the slag entrainment in liquid steel and the bubbles capture in the initial solidified shell, both of which are associated with the quality of the final product. This paper presents a numerical study of the turbulent flow with a top free surface in the continuous casting mold at a meso-scale level by a three-dimensional combined approach of Free Surface Lattice Boltzmann Method and Large Eddy Simulation (FSLBM-LES). The validity of the model is verified by the good agreement between the calculated results and the measurements from various water experiments in terms of the flow velocity and free surface profile. The mathematical model is then used to reveal the transient and spatiotemporal asymmetric characteristics associated with the transient flow field and the free surface fluctuation, although the steady state operation is considered during the continuous casting process. The results show that the locations of the jets of liquid steel from the two out ports of the Submerged Entry Nozzle (SEN) always fluctuate alternatively within a certain range, and periodically deviate from the design angle of the SEN within the same time period. The oscillating behavior of the jets promotes the asymmetric flow patterns and multi-scale vortices at both sides of the SEN. By introducing the Q-criterion in the results analysis, the formation, development, and shedding of the coherent structure (CS) of the turbulent flow are quantitatively characterized. The interaction between the transient flow patterns and the fluctuations of the top free surface as well as the evolution of the transient profile and velocities of the free surface are also demonstrated. The results obtained from the current study suggest that the FSLBM-LES model offers a promising way to study the complex flows and related transfer phenomena in the continuous casting process.

Owing to the smaller cross‐sectional size of the billet, the effect of the position of the submerged entry nozzle (SEN) on the fluid flow in a curved mold is more prominent. The transient fluid flow, heat transfer, and solidification behavior at different nozzle positions and mold electromagnetic stirring (M‐EMS) are investigated using a 3D transient mathematical model. The symmetry index, S, is introduced to quantitatively evaluate the symmetry of the flow field. When the SEN is offset to the outer curve, S is the highest, the flow field mixing is the best, and the liquid level fluctuation is minimal. When the SEN is offset to the inner curve, S is the lowest, and the washing of the solidified shell on the inner curve side is more significant, causing the solidified shell thickness on the inner curve to be thinner, which can easily cause steel breakout accidents. The M‐EMS can improve the uneven flow field caused by the nozzle position. In actual production, the SEN can be appropriately offset to the outer curve, and the application of M‐EMS can improve the flow field distribution of molten steel.

In continuous casting, the flow structure of the liquid steel in the mould and the two-phase distribution in the submerged entry nozzle (SEN) are crucial for the quality of the produced steel. In order to effectively control the flow in the mould by electromagnetic brakes (EMBrs) and the injection of gas into the SEN, even a rough knowledge of the flow structure would be very helpful. In the framework of the TOMOCON project, the contactless inductive flow tomography (CIFT) and the mutual inductance tomography (MIT) will be integrated into a control loop for slab casters. This control loop will be developed and implemented at the Mini-LIMMCAST facility, which is available at the Helmholtz-Zentrum Dresden - Rossendorf. In this paper a short overview of this project will be given.

The heat transfer and stress state of thin slab have a significant impact on quality of slab in the solidification process of continuous casting. A two-dimensional mathematical model of heat transfer, which has considered the characteristics of solidification and heat transfer and the influence of secondary cooling system and equipment on solidification process, has been established to analysis temperature distribution of cross-section and main factors impacting on temperature distribution. A two-dimensional thermal-elastic-plastic stress model has been established to analysis the stress and strain distribution of thin slab in the continuous casting, and it uses the two-dimensional slicing method in a moving coordinate and finite element method for solving the model. The simulation results can provide a theoretical guide for the optimization of continuous casting process parameters and improvement of quality of thin slab.

Industrial thin slab casting and direct rolling processing started more than 25 years ago with the world's first compact strip production (CSP®). Since that time, CSP® and competing thin slab casting and direct rolling concepts have been developed to a standard process for hot strip production. Typical features of this process are the homogeneous structural and mechanical properties all along the strip. The product range covers low carbon, as well as medium and high carbon steel grades comprising IF, HSLA, API, electrical, and AHSS multiphase steel grades. Hot strip from thin slab can be easily further processed to cold rolled and/or surface treated strip. A special feature is thin hot strip that may substitute cold rolled strip. Today, process and material developments, for example, go for rise in productivity, thinner gauge hot strip, as well as thicker line pipe and 3rd generation AHSS grades combining higher strength and ductility. The quality- and product-related advantages of thin slab casting and direct rolling technology are explained in this contribution at the example of the CSP® process.