In Situ Formed Gradient Composite Solid Electrolyte Interphase Layer for Stable Lithium Metal Anodes.

Li metal is an ideal anode material for next-generation energy storage devices due to its extremely high theoretical specific capacity and the lowest negative electrochemical potential [1,2]. However, uncontrolled Li dendrite growth and the side reaction between Li metal and electrolytes have prevented its practical application in rechargeable Li metal batteries. In our contributions, artificial solid electrolyte interphase (SEI) layer and 3D current collector have been developed to address these issues [3,4]. In this presentation, we will introduce an artificial Li3PO4 SEI layer [3] fabricated by in situ reaction of polyphosphoric acid (PPA) with Li metal and its native film (Li2CO3, LiOH, and Li2O). The partial dissolution of the Li native film and formation of the SEI layer lead to a porous structure of the Li surface, thereby promoting Li dendrite formation and growth. In the ingenious design, the native film of Li metal is replaced by the stable and uniform Li3PO4 SEI layer. The artificial Li3PO4 SEI layer with thickness of 50 nm exhibits a smooth surface and a high Young’s modulus (10-11 GPa). Furthermore, the artificial Li3PO4 SEI layer is demonstrated to be stable in the electrolyte and during cycling in a Li|LiFePO4 battery system. The Li-conducting Li3PO4SEI layer can achieve uniform Li deposition, and reduce the side reaction between the Li metal and the electrolyte. Thus, the artificial SEI strategy we described is a promising route to tackle the intrinsic problems of Li metal anodes and other metal based anodes. Furthermore, we will show that Li metal anode can be accommodated in the reserved pores of the 3D current collector [4] with a submicron skeleton and high surface area, thereby suppressing the Li dendrite growth and solving the associated problems of Li metal anodes. Because of the high electroactive area of the submicron 3D structure, the 3D current collector can improve the Li plating/stripping efficiency and reduce the resistance of the Li metal anode. The utilization of the 3D architecture to accommodate the Li metal anode will highlight the importance of rational design of current collectors and reveal a new avenue for developing Li metal anodes with a long lifespan. References Y.-X. Yin, S. Xin, Y.-G. Guo, L.-J. Wan, Angew. Chem. Int. Ed. 2013, 52, 13186.W. Xu, J. L. Wang, F. Ding, X. L. Chen, E. Nasybutin, Y. H. Zhang, J. G. Zhang, Energ. Environ. Sci. 2014, 7, 513.N.-W. Li, Y.-X. Yin, C.-P. Yang, Y.-G. Guo, Adv. Mater. 2015, DOI: 10.1002/adma.201504526.C.-P. Yang, Y.-X. Yin, S.-F. Zhang, N.-W. Li, Y.-G. Guo, Nat. Commun. 2015, 6, 8058

Electronic devices have been advanced rapidly over the last few decades with improved performance through high-level integration. Lithium ion batteries (LIB), which is representative rechargeable energy storage system, is increasingly demanding to high-energy-density storage system for the stable operation of high performance devices like mobile, laptop, etc. In addition, a recent quantum leap in electronic vehicles (EVs) require to energy storage system with long cycling stability incomparable to previous electronic devices. To achieve high performances and long lifetime, the use of lithium metal is one of attractive anode for as LIBs, because Li metal has high theoretical specific capacity of 3860 mAh/g, low redox potential of -3.04V (verse the standard hydrogen electrode) and low gravimetric density of 0.59 g/cm3. Nevertheless, since Li metal anode has the lithiation-delithiation mechanism of the ‘hostless’ electrochemical plating/stripping unlike the conventional graphite anode, it is confronted with serious problems occurred from uncontrollable interfacial reaction between surface of lithium metal anode and electrolyte applying to traditional LIB system; that is (1) the uncontrollable formation of solid electrolyte interphase (SEI) layer limitless volume expansion of Li metal anode (2) the dendritic growth and isolation of Li interface derived from inhomogeneous deposition of Li+ ion flux (3) the Li surface fracture induced by heterogeneously plated Li+ ion. Through these process, repetitive formation of undesirable SEI layer at surface of Li anode make fresh electrolyte dissipation and concurrently the anode surface becomes more distorted. These side-phenomena strongly correlate with low coulombic efficiency and decreasing lifetime of lithium metal battery (LMB) system where lithium metal is used as anode. In this works, in a dimensional aspect, to solve such problem mentioned above through stabilizing of surface of lithium metal anode, we introduce Janus-faced protective layer (JPL) as gel polymer electrolyte. JPL was composed with dual layer of Ni (3~7μm) embedded poly(vinylidene fluoride-co-hexafluoropropylene) (PVdF-HFP) and bare PVdF-HFP through simple casting method. The process of preparing JPL membrane is so simple to instantly bring in existing roll-to-roll process, and it is also possible to make a low cost process considered relatively low nickel price. In terms of mechanical property, it is based on flexible polymer and shows the merit of being foldable enough to able origami. In addition, JPL play a role of protection of Li metal anode. JPL has two functionalities. The metal part of JPL directly contacted with anode, and this layer was frameworks for preventing irregular SEI layer formation through inward plating of Li ion, the polymer part is stable state enough to be used as a gel polymer electrolyte. When lithium metal anode is subjected to cycle-test while keeping in contact with the nickel side of JPL membrane, Scanning electron microscope (SEM) image showed that the surface of lithium metal anode was very clean without any fluctuation compared to the case where only polypropylene (PP) separator was used. (Figure. 1) Moreover, as shown in Figure 2., the LMB system applied JPL show high stability of tolerable overvoltage within 5mV, 15mV even at high-current of 10mA/cm2, 20mA/cm2, respectively, in Li//JPL/JPL//Li symmetric cell. These results are attributable to effective function of each layer as mentioned earlier. JPL consists of two layer, the tough and adhesive nature of PVdF-HFP prevents the polymer part from being damaged or torn by dendritic growth and simultaneously ensure that metal part functions as robust framework for SEI layer formation without escaped particle from the membrane. This frameworks induce the SEI layer, which can act as a resistive element, to grown in the metal part while surface of Li metal anode become get out of main subject from the SEI layer formation. By virtue of that property, JPL has not allow forming resistive elements on the surface of Li metal anode, preventing the voltage rising up due to the formation of resistive elements at surface, so tolerability of overvoltage with clean surface of anode is maintained. In conclusion, the model study of nickel micro-particle/PVdF-HFP composite suggests the straightforward direction of protective layer to apply lithium metal as anode in LIB system with alleviating the problem caused by the ‘hostless’ property of lithium metal anode. Thus, when JPL is introduced to a LIB system, it shows a fairly positive possibility for high performance Lithium metal battery. Figure 1

The lithium metal anode is regarded as a promising candidate in next-generation energy storage devices. Lithium nitrate (LiNO3 ) is widely applied as an effective additive in ether electrolyte to increase the interfacial stability in batteries containing lithium metal anodes. However, because of its poor solubility LiNO3 is rarely utilized in the high-voltage window provided by carbonate electrolyte. Dissolution of LiNO3 in carbonate electrolyte is realized through an effective solvation regulation strategy. LiNO3 can be directly dissolved in an ethylene carbonate/diethyl carbonate electrolyte mixture by adding trace amounts of copper fluoride as a dissolution promoter. LiNO3 protects the Li metal anode in a working high-voltage Li metal battery. When a LiNi0.80 Co0.15 Al0.05 O2 cathode is paired with a Li metal anode, an extraordinary capacity retention of 53 % is achieved after 300 cycles (13 % after 200 cycles for LiNO3 -free electrolyte) and a very high average Coulombic efficiency above 99.5 % is achieved at 0.5 C. The solvation chemistry of LiNO3 -containing carbonate electrolyte may sustain high-voltage Li metal anodes operating in corrosive carbonate electrolytes.

Solvent-derived inorganic F and N-rich solid electrolyte interface for stable lithium metal batteries

The increasing demand for high-specific-energy lithium batteries has stimulated extensive research on the lithium metal anode owing to its high specific capacity and low electrode potential. However, the lithium metal will irreversibly react with the electrolyte during the first cycling process, forming an uneven and unstable solid electrolyte interphase (SEI) layer, which results in the non-uniform deposition of Li ions and thus the formation of lithium dendrites. This could cause a battery short circuit, resulting in safety hazards such as thermal runaway. In addition, the continuous rupture and repair of the SEIs during the repeated charge/discharge processes will constantly consume the active lithium, which leads to a significant decrease in battery capacity. An effective strategy to address these challenges is to design and construct ideal artificial SEIs on the surface of the lithium metal anode. This review analyzes and summarizes the mathematical modeling of SEI, the functional characteristics of SEIs with different components, and finally discusses the challenges faced by artificial SEIs in practical applications of lithium metal batteries and future development directions.

Artificial solid electrolyte interphase (SEI) layers have been widely regarded as an effective protection for lithium (Li) metal anodes. In this work, an artificial SEI film consisting of dense Li6.4La3Zr1.4Ta0.6O12 (LLZTO) nanoparticles and polymerized styrene butadiene rubber is designed, which has good mechanical and chemical stability to effectively prevent Li anode corrosion by the electrolyte. The LLZTO-based SEI film can not only guide Li to uniformly deposit at the interface but also accelerate the electrochemical reaction kinetics due to its high Li+ conductivity. In particular, the high Young's modulus of the LLZTO-based SEI will regulate e- distribution in the continuous Li plating/stripping process and achieve uniform deposition of Li. As a consequence, the Li anode with LLZTO-based SEI (Li@LLZTO) enables symmetric cells to demonstrate a stable overpotential of 25 mV for 600 h at a current density of 1 mA cm-2 for 1 mA h cm-2. The Li@LLZTO||LFP (LiFePO4) full cell exhibits a capacity of 106 mA h g-1 after 800 cycles at 5 C with retention as high as 90%. Our strategy here suggests that the artificial SEI with high Young's modulus effectively inhibits the formation of Li dendrites and provides some guidance for the design of higher performance Li metal batteries.

Lithium (Li) metal batteries (LMBs) are enjoying a renaissance due to the high energy densities. However, they still suffer from the problem of uncontrollable Li dendrite and pulverization caused by continuous cracking of solid electrolyte interphase (SEI) layers. To address these issues, developing spontaneously built robust polymer-reinforced SEI layers during electrochemical conditioning can be a simple yet effective solution. Herein, a robust homopolymer of cyclic carbonate urethane methacrylate is presented as the polymer matrix through an in situ polymerization method, in which cyclic carbonate units can participate in building a stable polymer-integrated SEI layer during cycling. The as-investigated gel polymer electrolyte (GPE) assembled LiCoO2 /Li metal batteries exhibit a fantastic cyclability with a capacity retention of 92% after 200 cycles at 0.5 C (1 C = 180 mAh g-1 ), evidently exceeding that of the counterpart using liquid electrolytes. It is noted that the anionic ring-opening polymerization of the cyclic carbonate units on the polymer close to the Li metal anodes enables a mechanically reinforced SEI layer, thus rendering excellent compatibility with Li anodes. The in situ formed polymer-reinforced SEI layers afford a splendid strategy for developing high voltage resistant GPEs compatible with Li metal anodes toward high energy LMBs.

Recent progress in carbon/lithium metal composite anode for safe lithium metal batteries

Lithium (Li) metal, a typical alkaline metal, has been hailed as the "holy grail" anode material for next generation batteries owing to its high theoretical capacity and low redox reaction potential. However, the uncontrolled Li plating/stripping issue of Li metal anodes, associated with polymorphous Li formation, "dead Li" accumulation, poor Coulombic efficiency, inferior cyclic stability, and hazardous safety risks (such as explosion), remains as one major roadblock for their practical applications. In principle, polymorphous Li deposits on Li metal anodes includes smooth Li (film-like Li) and a group of irregularly patterned Li (e.g., whisker-like Li (Li whiskers), moss-like Li (Li mosses), tree-like Li (Li dendrites), and their combinations). The nucleation and growth of these Li polymorphs are dominantly dependent on multiphysical fields, involving the ionic concentration field, electric field, stress field, and temperature field, etc. This review provides a clear picture and in-depth discussion on the classification and initiation/growth mechanisms of polymorphous Li from the new perspective of multiphysical fields, particularly for irregular Li patterns. Specifically, we discuss the impact of multiphysical fields' distribution and intensity on Li plating behavior as well as their connection with the electrochemical and metallurgical properties of Li metal and some other factors (e.g., electrolyte composition, solid electrolyte interphase (SEI) layer, and initial nuclei states). Accordingly, the studies on the progress for delaying/suppressing/redirecting irregular Li evolution to enhance the stability and safety performance of Li metal batteries are reviewed, which are also categorized based on the multiphysical fields. Finally, an overview of the existing challenges and the future development directions of metal anodes are summarized and prospected.

Lithium (Li) metal anodes have become an important component of the next generation of high energy density batteries. However, the Li metal anode still has problems such as Li dendrite growth and unstable solid electrolyte interface layer. Herein, we present a functional electrolyte additive (PANHF) successfully synthesized from acrylonitrile and hexafluorobutyl methacrylate via a polymerization reaction. With extensive analytical characterization, it is found that the PANHF can improve the reversibility and Coulombic efficiency of the Li deposition/dissolution reaction and prevent the growth of Li dendrites by forming a solid electrolyte interphase rich in organic matter on the outer layer and LiF on the inner layer. The results show that the cycling performance of the Li/Li cell was greatly improved in the electrolyte containing 0.5 wt % PANHF. Specifically, the cycling stability of more than 700 cycles was achieved at a current density of 1.0 mA cm-2. Moreover, the Li/NCM811 cell with 0.5 wt % PANHF has a higher capacity of 137.7 mA h g-1 at 1.0 C and a capacity retention of 83.41% after 200 cycles. This work highlights the importance of protecting the Li metal anode with functional bipolymer additives for next-generation Li metal batteries.

The use of lithium (Li) metal anodes has been reconsidered because of the necessity for a higher energy density in secondary batteries. However, Li metal anodes suffer from ‘dead’ Li formation and surface deactivation which consequently form a porous layer of redundant Li aggregates. In this work, a fibrous metal felt (FMF) as a three-dimensional conductive interlayer was introduced between the separator and the Li metal anode to improve the reversibility of the Li metal anode. The FMF can facilitate charge transfer in the porous layer, rendering it electrochemically more active. In addition, the FMF acted as a robust scaffold to accommodate Li deposits compactly in its interstitial sites. The FMF-integrated Li metal (FMF/Li) electrode operated with a small polarisation even at a current density of 10 mA cm−2, and it exhibited a seven times longer cycle-life than that of an FMF-free Li electrode in a symmetric cell configuration. A Li metal battery (LMB) using the FMF/Li electrode and a LiFePO4 electrode exhibited a two-fold increase in cycling stability compared with that of a bare Li metal electrode, demonstrating the practical effectiveness of this approach for high performance LMBs.

LiF-rich and self-repairing interface induced by MgF2 engineered separator enables dendrite-free lithium metal batteries

A widely applicable strategy to convert fabrics into lithiophilic textile current collector for dendrite-free and high-rate capable lithium metal anode

Constructing {110}‐textured lithium (Li) metal anodes is a promising strategy to extend battery life. While preparation of such anodes has been the subject of a few studies, their focus has been exclusively on thermodynamically‐driven (equilibrium) strategies. Through a systematic screening of bath conditions, the study reported here identifies a novel kinetically‐driven protocol that enhances the volume fraction of {110} texture by more than fivefold compared to equilibrium approaches. The protocol involves Li deposition at high current densities or low temperatures in a commonly used LiNO3‐containing ether‐based electrolyte. Columnar {110}‐oriented grains are formed through a growth rate selection process arising from the stronger electronic coupling and faster electron transfer rate between Li(110) and Li+ cations compared to other lattice planes. LiNO3 plays a crucial role by inhibiting the deposition on the Li(110) plane less than the other planes. Simple bath condition adjustments yield optimized {110}‐textured Li anodes with improved plating/stripping homogeneity that suppresses dendrite formation and electrolyte consumption, resulting in extended cycle life in lean‐electrolyte full cells. This kinetically‐driven approach offers mechanistic insight into Li texture formation and a promising route to high‐performance Li metal anodes.

Lithium (Li) metal batteries have long been deemed as the representative high‐energy‐density energy storage systems due to the ultrahigh theoretical capacity and lowest electrochemical potential of Li metal anode. Unfortunately, the intractable dendritic Li deposition during cycling greatly restrains the large‐scale applications of Li metal anodes. Recent advances have been explored to address this issue, among which a specific class of electrolyte additives for electroplating is deeply impressive, as they are economic and pragmatic. Different from the conventional additives that construct solid electrolyte interphase (SEI) layer on anodes, they make dendrite‐free Li metal anodes feasible through altering Li plating behavior. In this research news article, the interlinked principles between industrial electroplating and Li deposition are firstly illustrated. The featured effects of electroplating additives on regulating Li plating morphology are also summarized and mainly divided into three categories: co‐deposition with Li cation, coordination with Li cation, and leveling effect of Li films. Furthermore, the mechanism exploration or derivative use of electroplating additive for dendrite suppression and potential research directions are proposed, with emphasizing that industrial electroplating might enable Li metal anode to scalable battery techniques and spread to metal battery systems beyond Li.