The paper deals with the concept of how to regulate structure formation in the interfacial transition zone (ITZ) between the Ordinary Portland Cement (OPC) matrix and basalt to ensure the durability of basalt fiber-reinforced concretes. It has been demonstrated that the alkali–silica reaction (ASR) can be transformed from a destructive (negative) process into a constructive one in OPC concrete through activation by sodium water glass combined with the incorporation of an Al2O3-containing additive, namely metakaolin. Alkaline activation increased the compressive strength of OPC basalt fiber-reinforced concrete by 1.6–1.9 times. The formation of stable zeolite-like hydration products within the Na2O-CaO-Al2O3-SiO2-H2O system promoted self-healing of the ITZ. This resulted in a 5.6-fold increase in ITZ microhardness compared to the cement matrix, as well as transforming expansion into shrinkage of concrete with a final value of 0.01 mm/m after 360 days. The structure-forming processes in the ITZ ensured a 1.14-fold increase in the compressive strength of 180-day alkali-activated OPC basalt fiber-reinforced concrete compared to its 30-day strength, in contrast to a 0.92-fold decrease in the strength of the non-modified OPC analog under conditions accelerating the development of ASR.

In recent years, there has been a notable increase in commercial demand for natural fibers. Consequently, numerous studies have concentrated on formulating innovative industrial production methodologies for natural fibers, with a particular emphasis on the environmental sustainability of production processes. Among natural fiber sources, bamboo has emerged as a leading candidate, attracting considerable interest due to its exceptional renewability, rapid growth, and low cultivation requirements. The contemporary industrial methodologies employed in the extraction of cellulose from bamboo frequently entail the utilization of concentrated solutions of strong acids and bases, often at elevated temperatures and with extended treatment durations. These processes generate highly polluting waste from mineral acids and bases, posing significant environmental challenges and ecosystem damage. In response to the prevailing concerns, there has been a marked increase in the focus on environmentally friendly techniques that combine enzymatic treatments, selective chemical reagents, and optimized mechanical processes. These processes facilitate the extraction of high-quality bamboo fibers, which are suitable for utilization in the textile industry and have the potential to replace synthetic fibers. This work demonstrates the efficacy of methodologies employing more diluted solutions than conventional approaches. Specifically, this study utilizes a weak base, such as NH4OH, in conjunction with hydrothermal extraction. It is therefore possible for dilute weak base solutions to yield natural fibers after a relatively brief period of processing, typically just a few hours.

Construction technologies and materials engineering are collaborating to develop new solutions that enhance energy efficiency. One such solution is thermal barriers filled with phase change material. Thanks to their thermal properties, these innovative barriers are being used in an increasing number of construction projects. Additive manufacturing enables the production of architected thermal barriers with controlled cellular topologies and customized heat transfer pathways. This study investigates the thermal performance of lightweight partitions produced using masked stereolithography (m-SLA) 3D printing, focusing on two geometries: open-cell Kelvin structures and closed-cell honeycomb structures. Two strategies for incorporating phase change material were evaluated: direct addition of 10% and 30% paraffin oil by weight to the photopolymer resin and post-print filling of cellular voids with a PCM-based gel. The aim was to establish the effect of topology and PCM distribution on steady-state thermal parameters and transient temperature stabilization. Experimental testing under cyclic heating–cooling conditions revealed that increasing paraffin oil content significantly improves thermal performance. The open-cell Kelvin structure with 30% PCM exhibited the lowest thermal conductivity (λ = 0.0289 W/(m·K)) and the highest thermal resistance (R = 0.697 m2·K/W). Honeycomb structures achieved λ = 0.0360 W/(m·K) and R = 0.590 m2·K/W at the same PCM content. Transient analysis demonstrated enhanced temperature stabilization, with maximum ΔT values of 29.55 K (30% PCM) and 28.61 K (honeycomb 30%). These results confirm that the geometry produced by additive manufacturing plays a decisive role in governing heat transfer and latent heat utilization in PCM-based thermal barriers.

This study evaluates the textile potential of five underexplored Agave varieties (Agave salmiana crassispina, A. salmiana salmiana, A. ingens marginata, A. tecta, and A. mapisaga) through combined analyses of extraction behaviour, microstructure, and single-fibre mechanical performance. Fibres extracted from basal, middle, and upper leaf sections were characterised using scanning electron microscopy (SEM) and single-fibre tensile testing under controlled conditions. All varieties produced spinnable fibres and exhibited significant longitudinal variability in mechanical behaviour along the leaf axis (p < 0.05). Mechanical performance depended strongly on both species and leaf position, with fibres from the middle leaf section generally showing higher tenacity. Variations in Young’s modulus reflected differences in fibre maturity and internal microstructural organisation. Fractographic observations revealed predominantly brittle fracture with microfibrillar rupture and longitudinal fibrillation. Overall, the results demonstrate that agave species and leaf position are key parameters governing fibre performance. These agave varieties therefore represent promising candidates for sustainable textile applications, provided that appropriate fibre selection and blending strategies are implemented to ensure homogeneous yarn properties.

The article examines the waste management challenges associated with basalt fiber-based mineral insulation materials generated during the production of thermal insulation products. In response to the environmental and economic issues linked to their disposal, a chemical processing approach is proposed to convert this waste into a mineral powder suitable for construction applications, particularly as an additive in asphalt concrete. A detailed technological scheme of the chemical treatment process is presented, and the optimal proportions of waste, water, and electrolyte (sulfuric acid), along with the corresponding processing conditions, are identified. The chemical and mineralogical composition of the raw materials and the resulting powder are investigated, and laboratory tests are carried out confirming its suitability as an active mineral additive. The chemical and mineralogical characteristics of the raw waste and resulting product are analyzed using XRD, SEM-EDS, and standard physical tests. In addition, the proposed technology provides a notable reduction in waste volume, thereby decreasing the load on landfills and contributing to more sustainable resource utilization.

This study investigates the behaviour of Compressed Earth Cylinders (CECs) and Compressed Earth Blocks (CEBs) during direct compression tests and examines the influence of aspect ratio and the effects of platen restraint. The experimental investigation utilises two soil types and examines the impact of jute fibre reinforcement on the failure mechanism of CECs with aspect ratios ranging from 0.50 to 2.00. Through experimental analysis and numerical modelling, the effects of platen restraint are examined, and a novel hypothesis of intersecting cones is presented. The results show that specimens with a lower aspect ratio exhibited higher compressive strength due to confinement caused by platen restraint. Moreover, this research has derived new aspect ratio correction factors that enable conversion from Apparent Compressive Strength (ACS) to Unconfined Compressive Strength (UCS) of unstabilised and fibre-reinforced CECs. The experimental results indicate that the derived conversion factor of 0.861 allows for the prediction of CEB strength from CEC specimens with an accuracy of 2.7%. Furthermore, the addition of jute fibres at a 0.25% dosage increased the Apparent Compressive Strength across all aspect ratios. The outcome of this research recommends a standard approach to the application of aspect ratio correction factors when interpreting and reporting the compressive strength of CECs and CEBs.

The incorporation of recycled tyre polymer fibres (RTPF) in cementitious composites provides an effective and sustainable approach in tyre waste management while offering potential benefits in mitigating early-age volume deformations. This study evaluates the influence of RTPFs, used in dry (RTPFd) and pre-wetted (RTPFw) states, on key hydration processes governing autogenous shrinkage in cement pastes with w/c of 0.4 and 0.22. The results show that RTPF reduced workability and altered the setting process due to the fibre–matrix mechanical interactions. Incorporation of RTPFs induced changes in water distribution at the fibre surface, delaying self-desiccation and maintaining higher internal relative humidity. While RTPFs offer a beneficial reduction in autogenous shrinkage by 12–41% in mixtures with w/c of 0.4 and by 15–34% in mixtures with w/c of 0.22, RTPFs also increased porosity, which contributed to a reduction in 28-day compressive strength of up to 16%. These findings highlight the dual effect of RTPF on early-age performance and provide insight into their potential application in sustainable cementitious composites.

In the last decades, composite materials made of synthetic fibers embedded in organic or inorganic matrices have been successfully used for strengthening reinforced-concrete and masonry buildings. The scientific community is currently discussing the low sustainability of these materials and their environmental impact due to the production process, the life cycle, and the generation of potentially harmful waste. In this context, the use of natural textiles represents a promising solution, alternative to conventional synthetic fibers, aimed at designing an innovative composite material obtained from renewable resources with no energy consumption and greatly reducing the impact of building activities on the environment. In this paper, an experimental assessment of ten different natural textiles is presented in order to compare their mechanical properties for possible use in innovative, eco-friendly composite materials. Mechanical tensile tests were performed on the ten different textiles before and after an all-natural protective treatment referred to as the “hornification” process. Treatment-induced changes in the fiber morphology were also analyzed using a scanning electron microscope (SEM), which provided high-resolution images of the surface and cross-sectional area of the fibers. Considering that the current demand for sustainable building materials capable of ensuring a greener future for the construction industry is on the rise, the promising results obtained in this study could be useful to the academic community and building industry.

Particulate matter (PM) and volatile organic compounds (VOCs) are major air pollutants that can cause significant risks to public health. To mitigate exposure, fibrous filters have been widely utilized for air purification. In this study, we developed electrospun silk fibroin/poly (ethylene oxide)/cyclodextrin (SF/PEO/CD) nanofibers as multifunctional air filters capable of efficiently reducing PM2.5 and degrading VOCs. The resulting SF/PEO/10CD demonstrated the best multifunctional filtration performance, achieving PM2.5 capture efficiencies of 91.3% with a minimal pressure drop of 4 Pa and VOC removal efficiency of 50%. These characteristics highlight the potential of the SF/PEO/10CD nanofiber with effective, multifunctional properties and environmental benefits for sustainable air filtration application.

As part of an implementation in the Peruvian textile industry, the use of different sources to obtain blue hues in alpaca fiber has taken on a prominent role. The present study investigated the optimization of the dyeing process of alpaca fibers using indigo carmine as dye. The methodology was based on a central composite design (CCD) and response surface methodology (RSM) with color strength (K/S) as response variable. The results demonstrate that the independent variables significantly affected the color strength (K/S). In this context, an increase in both mordant concentration (3.9887 g/L) and dyeing temperature (95 °C), coupled with lower exhaust time (30.0019 min), enhanced levels of superficial dye adsorption. Additionally, color fastness properties provided tolerable values according to the gray scale. In conclusion, the optimization of the dyeing process of alpaca fibers using indigo carmine enabled the achievement of a blue shade with satisfactory fastness properties in the fiber yarns.